This study aims to practically determine the optimum proportion of aggregates to attain the desired strength of geopolymer concrete (GPC) and then compare the results using established analytical particle packing methods. The investigation further aims to assess the influence of various amounts of recycled aggregate (RA) on properties of low-calcium fly ash-based GPC of grade M25.

Fine and coarse aggregates were blended in various proportions and the proportion yielding maximum packing density was selected as the optimum proportion and they were compared with analytical models, such as Modified Toufar Model (MTM) and J. D. Dewar Model. RAs for this study were produced in laboratory and they were used in various amounts, namely, 0%, 50% and 100%. 12M NaOH solution was mixed with Na₂SiO₃ in the ratio of 1:2. The curing of concrete was done at the temperatures of 60° and 90 °C for 24, 48 and 72h.

The experimentally obtained optimum proportion of coarse to fine aggregate was 60:40 for all amounts of RA. Meanwhile, MTM and Dewar Model resulted in coarse aggregate to fine aggregates as 40:60, 45:55, 55:45 and 55:45, 35:65, 60:40, respectively, for 0% 100% and 50% RAs. The compressive strength of GPC elevated with the increase in curing regime. In addition, the ultrasonic pulse velocity also displayed a similar trend as that of strength.

The GPC with 50% RAs may be considered for use, as it exhibited superior properties compared to GPC with 100% RAs and was comparable to GPC with natural aggregates. Furthermore, compressive strength is correlated with split tensile strength and ultrasonic pulse velocity.

The purpose of this paper is to investigate the effect of the replacement of natural coarse aggregate (NCA) with different percentages of recycled coarse aggregate (RCA) on properties of low calcium fly ash (FA)-based geopolymer concrete (GPC) cured at oven temperature. Further, this paper aims to study the effect of partial replacement of FA by ground granulated blast slag (GGBS) in GPC made with both NCA and RCA cured under ambient temperature curing.

M25 grade of ordinary Portland cement (OPC) concrete was designed according to IS: 10262-2019 with 100% NCA as control concrete. Since no standard guidelines are available in the literature for GPC, the same mix proportion was adopted for the GPC by replacing the OPC with 100% FA and W/C ratio by alkalinity/binder ratio. All FA-based GPC mixes were prepared with 12 M of sodium hydroxide (NaOH) and an alkalinity ratio, i.e. sodium hydroxide to sodium silicate (NaOH:Na₂SiO₃) of 1:1.5, subjected to 90^°C temperature for 48 h of curing. The NCA were replaced with 50% and 100% RCA in both OPC and GPC mixes. Further, FA was partially replaced with 15% GGBS in GPC made with the above percentages of NCA and RCA, and they were given ambient temperature curing with the same molarity of NaOH and alkalinity ratio.

The workability, compressive strength, split tensile strength, flexural strength, water absorption, density, volume of voids and rebound hammer value of all the mixes were studied. Further, the relationship between compressive strength and other mechanical properties of GPC mixes were established and compared with the well-established relationships available for conventional concrete. From the experimental results, it is found that the compressive strength of GPC under ambient curing condition at 28 days with 100% NCA, 50% RCA and 100% RCA were, respectively, 14.8%, 12.85% and 17.76% higher than those of OPC concrete. Further, it is found that 85% FA and 15% GGBS-based GPC with RCA under ambient curing shown superior performance than OPC concrete and FA-based GPC cured under oven curing.

The scope of the present paper is limited to replace the FA by 15% GGBS. Further, only 50% and 100% RCA are used in place of natural aggregate. However, in future study, the replacement of FA by different amounts of GGBS (20%, 25%, 30% and 35%) may be tried to decide the optimum utilisation of GGBS so that the applications of GPC can be widely used in cast in situ applications, i.e. under ambient curing condition. Further, in the present study, the natural aggregate is replaced with only 50% and 100% RCA in GPC. However, further investigations may be carried out by considering different percentages between 50 and 100 with the optimum compositions of FA and GGBS to enhance the use of RCA in GPC applications. The present study is further limited to only the mechanical properties and a few other properties of GPC. For wider use of GPC under ambient curing conditions, the structural performance of GPC needs to be understood. Therefore, the structural performance of GPC subjected to different loadings under ambient curing with RCA to be investigated in future study.

The replacement percentage of natural aggregate by RCA may be further enhanced to 50% in GPC under ambient curing condition without compromising on the mechanical properties of concrete. This may be a good alternative for OPC and natural aggregate to reduce pollution and leads sustainability in the construction.

This paper aims to review the effect of using recycled aggregates (RA) on the properties of recycled aggregate concrete (RAC) following the steady rise in global demand for concrete and the large generation of construction and demolition waste.

This study reviewed relevant literature of research work carried out by previous researchers, leading to a deeper understanding of the properties of both RA and RAC. The properties of RA and RAC reported in the various studies were then compared to their corresponding natural aggregate (NA) and natural aggregate concrete, as well as the specifications provided in different codes of practice. In addition, the mix design methods appropriate to RAC and the cost implication of using RA were reviewed.

Findings show that the contribution of RA to strength appears inferior in comparison to NA. The shortcoming is attributed to the mortar attached to the RA, which raises its water absorption capacity and lowers its density relative to those of NA. However, it has been reported that the use of regulated quantity of RA, new mixing and proportioning methods, the addition of admixtures and strengthening materials such as steel fibres, can improve both mechanical and durability properties of RAC. Cost evaluation also showed that some savings can be realized by using RA instead of NA.

This research serves as a guide for future works and suggests that the use of RA as aggregate in new concrete is technically possible, depending on the mix design method adopted.

The purpose of this paper is to highlight the sustainability benefits of using demolition and industrial wastes as a replacement for aggregates and cement in traditional concrete mixes.

Crushed concrete from demolition sites served as a replacement for fine and coarse aggregate in some of the mixes at various ratios. In addition, ground granulated blast furnace slag, metakaolin, silica fume, and fly ash each served as a cement replacement for cement content in the mixes tested in this research at various rates. Compression strength tests, permeability, and thermal expansion tests were performed on various mixes to compare their performance to that of traditional mixes with natural aggregate, and with no cement replacement.

The compressive strength results indicated the suitability of using such demolition wastes as replacements in producing green concrete (GC) without hindering its mechanical characteristics significantly. In addition, the results indicated an enhancement in the mechanical characteristics of GC when replacing cement with pozzolanic industrial wastes and byproducts.

The research assesses the utilization of sustainable GC using recycled waste aggregate and byproducts.